SUBTRANSLUCENT SILICONE RUBBER FOR MOLDING
Characteristics:
● Compliance with FDA
● Superior physical, mechanical and electrical properties
● Excellent ageing resistance at temperature of -50℃ to 200℃
Main Applications:
● Various keypads, general industrial & civil silicone rubber products, sealing elements and miscellaneous parts
● General electric components
Typical Data：
|
Properties |
Product Data |
Test Method |
||||||
|
NE-130 |
NE-140 |
NE-150 |
NE-160 |
NE-170 |
NE-180 |
NE-190 |
||
|
Appearance |
Milk-white, subtranslucent, no obvious extraneous matter. |
Visual Inspection |
||||||
|
Density, g/cm3 |
1.07～1.11 |
1.10～1.14 |
1.13～1.17 |
1.16～1.20 |
1.19～1.23 |
1.20～1.24 |
1.22～1.26 |
ASTM D792 |
|
Hardness, Shore A |
30±2 |
40±2 |
50±2 |
60±2 |
70±2 |
80±2 |
86±2 |
ASTM D2240 |
|
Tensile Strength, MPa, ≥ |
6.0 |
6.5 |
8.0 |
8.0 |
7.5 |
7.0 |
4.5 |
ASTM D412 |
|
Elongation at Break, %, ≥ |
600 |
420 |
350 |
300 |
220 |
160 |
80 |
|
|
Tension Set, %, ≤ |
6 |
6 |
7 |
7 |
6 |
5 |
6 |
|
|
Tear Strength, Die C, kN/m, ≥ |
15 |
19 |
22 |
22 |
20 |
18 |
10 |
ASTM D624 |
|
Compression Set, 180℃*22h, ≤ |
45 |
35 |
30 |
30 |
30 |
30 |
25 |
ASTM D395 |
|
First-order linear shrinkage, % |
3.4～3.9 |
3.3～3.8 |
3.2～3.7 |
3.1～3.6 |
3.0～3.5 |
2.9～3.4 |
2.9～3.3 |
/ |
● Physical data in the above table is for reference only.
● Vulcanization condition: 175℃*5Min.
● Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy) hexane: 0.65%.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.
SUBTRANSLUCENT SILICONE RUBBER FOR EXTRUSION
Main Features:
● Compliance with FDA
● Superior physical, mechanical and electrical properties
● Excellent ageing resistance at temperature of -50℃ to 200℃
Main Application:
● Various silicone rubber tubes, shaped rubber strips and foam rubber strips, etc
Typical Data：
|
Properties |
Product Data |
Test Method |
||||
|
NE-240 |
NE-250 |
NE-260 |
NE-270 |
NE-280 |
||
|
Appearance |
Milk-white, subtranslucent, no obvious extraneous matter. |
Visual Inspection |
||||
|
Density, g/cm3 |
1.10～1.14 |
1.13～1.17 |
1.16～1.20 |
1.19～1.23 |
1.20～1.24 |
ASTM D792 |
|
Hardness, Shore A |
40±2 |
50±2 |
60±2 |
70±2 |
80±2 |
ASTMD2240 |
|
Tensile Strength, MPa, ≥ |
7.0 |
8.0 |
8.0 |
7.5 |
7.0 |
ASTM D412 |
|
Elongation at Break, %, ≥ |
450 |
400 |
320 |
250 |
150 |
|
|
Tension Set, %, ≤ |
9 |
9 |
9 |
9 |
8 |
|
|
Tear Strength, Die C, kN/m, ≥ |
19 |
20 |
22 |
20 |
20 |
ASTM D624 |
|
Compression Set, 180℃*22h, ≤ |
35 |
30 |
30 |
30 |
25 |
ASTM D395 |
● Physical data in the above table is for reference only.
● Vulcanization condition: 175℃* 5Min.
● Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy) hexane: 0.65%.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.
Related material download:
ROHS and Other Restricted Substances Test for Silicone Rubber
Substances of Very High Concern Test(SVHC) for Silicone Rubber
MSDS-Subtranslucent Silicone Rubber for Molding and Extrusion
Subtranslucent Silicone Rubber for Molding and Extrusion(TDS)