Characteristics:
●The compound features ultra-low volatility, with a volatile content of less than 0.5% after aging at 200°C for 4 hours. It is platinum-cured, and test specimens meet FDA, LFGB and GB4806.16 requirements without the need for secondary vulcanization.
Main Applications:
●Specializing in the manufacturing of molded and extruded silicone products for food contact and infant care industries.
Typical Data:
|
Properties |
Test Method |
||||||
|
NE-9000-30 |
NE-9000-40 |
NE-9000-50 |
NE-9000-60 |
NE-9000-70 |
|||
|
Appearance |
Transparent, no extraneous matter. |
Visual Inspection |
|||||
|
Density, g/cm3 |
1.08 |
1.12 |
1.13 |
1.17 |
1.20 |
ASTM D792 |
|
|
Vulcanization condition |
Two-component platinum vulcanization A：0.4%~0.5% B：0.5%~0.8%，120*10min |
||||||
|
Curing |
Hardness, Shore A |
31 |
44 |
49 |
62 |
68 |
ASTM D2240 |
|
Tensile Strength, MPa |
11.0 |
11.1 |
12.7 |
12.8 |
12.0 |
ASTM D412 |
|
|
Elongation at Break, % |
786 |
651 |
602 |
444 |
363 |
||
|
Tension Set, % |
3.4 |
5.0 |
2.6 |
4.4 |
4.4 |
||
|
Tear Strength, Die C, kN/m |
18.2 |
22.3 |
26.2 |
27.7 |
28.3 |
ASTM D624 |
|
|
Rebound Resilience,% |
70 |
61 |
63 |
57 |
53 |
/ |
|
|
Volatile content (Test sample),200℃*4h, % |
0.3 |
0.3 |
0.3 |
0.3 |
0.3 |
||
● Physical data in the above table is for reference only.
● Ratio of curing agent: platinum vulcanization, 0.4 %~0.5% added for component A, 0.5% ~0.8%added for component B, 120℃*10Min.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.