● Compliance with FDA and LFGB.
● High grade of transparency and excellent physical properties and good processability.
Main Applications:
●Suitable for silicone rubber products with extremely high requirement for transparency, such as extruded transparent tubes.
Typical Data:
|
Properties |
Product Data |
|||||||
|
NE-9630T |
NE-9640T |
NE-9650T |
NE-9660T |
NE-9670T |
NE-9680T |
|||
|
Appearance |
Transparent, no extraneous matter. |
Visual Inspection |
||||||
|
Density, g/cm3 |
1.06～1.10 |
1.09～1.15 |
1.12～1.18 |
1.14～1.20 |
1.17～1.23 |
1.18～1.25 |
ASTM D792 |
|
|
Curing |
Vulcanization condition |
175℃*5min |
|
|||||
|
Hardness, Shore A |
30±2 |
40±2 |
50±2 |
60±2 |
70±2 |
80±2 |
ASTM D2240 |
|
|
Tensile Strength, MPa, ≥ |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
ASTM D412 |
|
|
Elongation at Break, %, ≥ |
600 |
500 |
400 |
400 |
300 |
200 |
||
|
Tension Set, %, ≤ |
10 |
10 |
10 |
10 |
10 |
10 |
||
|
Tear Strength, Die C, kN/m, ≥ |
15 |
20 |
25 |
25 |
25 |
20 |
ASTM D624 |
|
|
Two-component platinum vulcanization |
Vulcanization condition |
120℃*10min, A(0.3-0.4%), B(0.5-0.6%) |
|
|||||
|
Hardness, Shore A |
32±2 |
40±2 |
46±2 |
56±2 |
64±2 |
76±2 |
ASTM D2240 |
|
|
Tensile Strength, MPa, ≥ |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
ASTM D412 |
|
|
Elongation at Break, %, ≥ |
700 |
600 |
500 |
500 |
450 |
300 |
||
|
Tension Set, %, ≤ |
10 |
10 |
10 |
10 |
10 |
10 |
||
|
Tear Strength, Die C, kN/m, ≥ |
15 |
20 |
25 |
25 |
25 |
20 |
ASTM D624 |
|
|
Single component platinum vulcanization |
Vulcanization condition |
120℃*10min, (0.8-1.0%) |
|
|||||
|
Hardness, Shore A |
32±2 |
40±2 |
46±2 |
56±2 |
64±2 |
76±2 |
ASTM D2240 |
|
|
Tensile Strength, MPa, ≥ |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
9.0 |
ASTM D412 |
|
|
Elongation at Break, %, ≥ |
700 |
600 |
500 |
500 |
450 |
300 |
||
|
Tension Set, %, ≤ |
10 |
10 |
10 |
10 |
10 |
10 |
||
|
Tear Strength, Die C, kN/m, ≥ |
15 |
20 |
25 |
25 |
25 |
20 |
ASTM D624 |
|
● Physical data in the above table is for reference only.
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy) hexane: 0.65%, 175℃*5Min.
● Ratio of curing agent: platinum vulcanization, (0.3~0.4) % added for component A, (0.5~0.6) % added for component B, 120℃*10Min.
● Ratio of curing agent: Single component platinum vulcanization, (0.8~1.0) %, 120℃*10Min.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.
Related material download:
经济高透明气相胶High-Transparency Fumed Silicone Rubber NE-96X0T Series TDS