● The rubber material has an extremely low volatile content, with volatility below 0.5% after 200°C for 4 hours. It is platinum-cured, and the test samples can pass FDA and LFGB tests without secondary curing, meeting the testing requirements of GB4806.16-2025.
Main Applications:
● Molded and extruded silicone products for the food contact and infant .
Typical Data:
|
Properties |
Test Method |
|||||||
|
NE-9000-30 |
NE-9000-40 |
NE-9000-50 |
NE-9000-60 |
NE-9000-70 |
NE-9000-80 |
|||
|
Appearance |
Transparent, no extraneous matter. |
Visual Inspection |
||||||
|
Density, g/cm3 |
1.08 |
1.12 |
1.13 |
1.17 |
1.20 |
1.21 |
ASTM D792 |
|
|
Vulcanization condition |
Two-component platinum vulcanization A：0.4%~0.6% B：0.5%~1.2%，130℃*10min |
|||||||
|
Curing |
Hardness, Shore A |
31 |
42 |
49 |
62 |
68 |
78 |
ASTM D2240 |
|
Tensile Strength, MPa |
11.0 |
11.1 |
12.7 |
12.8 |
12.0 |
10.5 |
ASTM D412 |
|
|
Elongation at Break, % |
786 |
651 |
602 |
444 |
363 |
375 |
||
|
Tension Set, % |
3.4 |
5.0 |
2.6 |
4.4 |
4.4 |
6.0 |
||
|
Tear Strength, Die C, kN/m |
18.2 |
22.3 |
26.2 |
27.7 |
28.3 |
27.9 |
ASTM D624 |
|
|
Rebound Resilience,% |
70 |
61 |
63 |
57 |
53 |
50 |
/ |
|
|
Test sample volatile content 200℃*4h, % |
0.4 |
0.35 |
0.35 |
0.35 |
0.4 |
0.4 |
||
● Physical data in the above table is for reference only.
● Ratio of curing agent: platinum vulcanization, 0.4 %~0.6% added for component A, 0.5% ~1.2%added for component B, 130℃*10Min.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.
Post-cure Free Fumed Silicone RubbeNE-9000-X0 典型数据